Síntesis, caracterización estructural y eléctrica de películas de V2O5 .nH2O
V2O5 .nH2O films were characterized structurally, vibrationally, and electrically, as well as synthesized by the method of rapid cooling or quenching. The films submitted to thermal treatment among 100°C and 200°C during 24 hours showed slight variations in the crystal structure with a preferred ori...
| Autor Principal: | Londoño C., César Leandro |
|---|---|
| Otros Autores: | Hernández J., Carlos Vargas, Jurado, Fabián |
| Formato: | info:eu-repo/semantics/article |
| Idioma: | spa |
| Publicado: |
Universidad de San Buenaventura - Cali
2017
|
| Materias: | |
| Acceso en línea: |
1794-192X |
| Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
| Sumario: |
V2O5 .nH2O films were characterized structurally, vibrationally, and electrically, as well as synthesized by the method of rapid cooling or quenching. The films submitted to thermal treatment among 100°C and 200°C during 24 hours showed slight variations in the crystal structure with a preferred orientation along [a00]. The electrical conductance showed an Arrhenius type behavior, typical of semiconductor materials, with activation energies of 0.246( ± )0.001 eV for the sprinkle and 0.262( ± )0.002 eV for the film submitted to thermal treatment at 200°C for 24 hours. These energy values are very close to those reported for vanadium pentoxide. µ-Raman spectra at room temperature confirmed the presence of vibrational modes, typical of vanadium oxide. |
|---|